セルロースエステルの代表的な物性値
セルロースエステルの代表的な物性値です。(a)
横にスクロールしてご覧ください。
Product | Viscosityb | Intrinsic viscosity |
Acetyl (wt%) |
Butyryl (wt%) |
Propionyl (wt%) |
Hydroxyl (wt%) |
Specific gravity |
Tgc(℃) | Melting range(℃) | MWnd | |
---|---|---|---|---|---|---|---|---|---|---|---|
poise | sec | ||||||||||
Cellulose acetate butyrate | |||||||||||
CAB 171-15 | 57.37 | 19 | - | 29 | 18 | - | 1.1 | 1.26 | 161 | 230–240 | 65,000 |
CAB 321-0.1 | 0.38 | 0.1 | - | 17.5 | 32 | - | 1.3 | 1.2 | 127 | 165–175 | 12,000 |
CAB 381-0.1 | 0.38 | 0.1 | - | 13.5 | 38 | - | 1.5 | 1.2 | 123 | 155–165 | 20,000 |
CAB 381-0.5 | 1.9 | 0.5 | - | 13.5 | 38 | - | 1.5 | 1.2 | 130 | 155-165 | 30,000 |
CAB 381-2 | 8 | 2 | - | 13.5 | 38 | - | 1.3 | 1.2 | 130 | 171-184 | 40,000 |
CAB 381-20 | 76 | 20 | - | 13.5 | 37 | - | 1.8 | 1.2 | 141 | 195-205 | 70,000 |
CAB 500-5 | 19 | 5 | - | 3 | 51 | - | 1 | 1.18 | 96 | 165-175 | 57,000 |
CAB 531-1 | 5.6 | 2 | - | 3 | 50 | - | 1.7 | 1.17 | 115 | 135-150 | 40,000 |
CAB 551-0.01 | 0.038 | 0.02 | - | 2 | 52 | - | 2 | 1.16 | 85 | 127-142 | 10,000 |
CAB 551-0.2 | 0.76 | 0.2 | - | 2 | 52 | - | 1.8 | 1.16 | 101 | 130-140 | 30,000 |
CAB 553-0.4 | 1.14 | 0.3 | - | 2 | 47 | - | 4.8 | 1.2 | 136 | 150-160 | 20,000 |
Cellulose acetate propionate | |||||||||||
CAP 482-0.5 | 1.53 | 0.5 | - | 1.5 | - | 45 | 2.6 | 1.23 | 142 | 188-210 | 25,000 |
CAP 482-20 | 76.5 | 20 | - | 1.3 | - | 48 | 1.7 | 1.22 | 147 | 188-210 | 75,000 |
CAP 504-0.2 | 0.76 | 0.2 | - | 0.5 | - | 42.5 | 5 | 1.26 | 159 | 188-210 | 15,000 |
Cellulose acetate | |||||||||||
CA 398-3 | 11.4 | 3 | - | 39.8 | - | - | 3.5 | 1.31 | 180 | 230-250 | 30,000 |
CA 398-6 | 22.8 | 6 | - | 39.8 | - | - | 3.5 | 1.31 | 182 | 230-250 | 30,000 |
CA 398-10 | 38.0 | 10 | - | 39.8 | - | - | 3.5 | 1.31 | 182 | 230-250 | 35,000 |
CA 398-30 | 114 | 30 | - | 39.8 | - | - | 3.5 | 1.31 | 189 | 230-250 | 50,000 |
Eastman Solus™ performance additives | |||||||||||
Solus 2100 | - | - | 0.08 | 2 | 53 | - | 1.6 | 1.2 | 75 | - | - |
Solus 2300 | - | - | 0.095 | 19 | 30 | - | 1.6 | 1.22 | ~110 | - | - |
Results converted to poises (ASTM D1343) using the solution density for Formula A as stated in ASTM D817 (20% cellulose ester, 72% acetone, 8% ethyl alcohol).
b.Viscosity determined by ASTM
c. Glass transition temperature d. Number-average molecular weight values, MWn, are polystyrene-equivalent weights determined using size-exclusion chromatography.